Adhesive melt for edge banding UNIMELT 584-В

Order products
Adhesive melt for edge banding UNIMELT 584-В
Send and our managers will contact you to clarify the details of the order

Description and characteristics — Adhesive melt for edge banding UNIMELT 584-В

It is a Sythetic resins and EVA Based, thermoplastic hotmelt adhesive.

Application areas:

UNIMELT 584-B is a strong adhesive used for banding PVC,ABS,POLYESTER,HPL and Melamine edge tapes on edge banding machines.

Technical specifications:

Color : White
Appearance : Granular
Brookfield Viscosity : 75000 ± 25000mPa.s (spindle at 190ºC 29 50 rpm)
Softening Point : 103 ± 5 ºC

Application:

Humidity in Material : 8-10% Humidity in the Air : 65-75% Material and Environment Temperature: >15ºC Tank Temperature : 180-200 ºC Roller Temperature : 180-200 ºC

Usage:

Environment temperature must be around 15°C during the application process. Adhesive must be applied to one surface of the material to be adhered. Air humidity should be %65-75 and product humidity should be %8-10.

Packaging :

25 Kg Paper Bag

Shelf life :

Shelf life is 12 months at room temperature (18-20 °C).

Recommendations:

On undesirable oil and dust surfaces, it prevents the formation of a strong bond and the desired strength cannot be obtained.
The temperature inside the adhesive thank should be considered, and be controlled frequently due to changes in weather & conditions. During season changes adhesive temperature must be measured by thermometer devices.
The temperature of the application surface and environment must be higher than 15ºC Otherwise, successful results cannot be achieved due to faster drying time.
Adhesive tank should be cleaned frequently. The amount of the adhesive, which is applied on the surfaces, can vary due to type of the materials. Some undesired results may occur such as over usage and inadequate usage. In these cases, glue setting should be applied.
In case of giving a pause, adhesive temperature must be binded at 100-110°C to keep performance higher and a prevent glue from burning.